Radiata pine boards were coated with two different methods A and B both beginning with a hydro primer and finishing with a mat oil but method A using an acrylic high gloss coating and method B three layers of an acrylic sealer in between. The samples were subjected to aging processes for 144 h, 288 h, and 432 h by using UV-A 340 nm lamps. The CIE L*a*b* and CIE L*C*H* coordinates were determined (L*, a*, b*, C*, ho *, ΔE*), gloss (perpendicular ( ) and parallel (//) to the grain at 20°, 60°, and 85° angles) and surface adhesion strength via the pull-off method were tested before and after weathering. Results have shown that lightness (L*), decreases with weathering for both varnish applications with a higher decrease for the B coating system. Redness increased for both applications with no significant differences. At the same time there was a yellowing of the samples along the weathering period. Parallel and perpendicular gloss decreased for 20º and 60º angles while it increased for 85º angle. The adhesion strength of method A was higher and its decrease with weathering was smaller than for method B. Both varnish applications have proven to confer some protection against wood discoloration, but method A showed the best results and is therefore the best method to be used by radiata pine.
Description
Keywords
Artificial weathering color glossiness Pinus radia varnish applications wood discoloration