Percorrer por autor "Martins, Jorge"
A mostrar 1 - 2 de 2
Resultados por página
Opções de ordenação
- Formulation and Characterization of a Composite Coating Formulation Based on Acrylic Foam and Cork GranulesPublication . Monteiro, Sandra; Ferreira, Nuno; Paiva, Diana; Silva, Susana P.; Martins, Jorge; Carvalho, Luisa; Magalhães, Fernão D.Cork, the bark of Quercus suber L., in addition to presenting several notable physicalmechanical properties, possesses a distinctive look and feel that make it attractive for interior surfaces, such as in furniture, wall paneling, or flooring. This work envisaged the development of a coating based on cork granules, a subproduct from the wine stopper industry, capable of creating a smooth surface similar to natural cork. In order to avoid the high rugosity that characterizes surfaces coated with paints that incorporate cork granules, a new solution was developed, based on a foamed acrylic binder, applied by knife coating. The foam formulation was successfully optimized, using appropriate additives and resorting to mechanical agitation to promote the generation of air bubbles. The addition of cork granules did not hinder foam stability, and the final coating displayed the intended visual and sensory characteristics. Dynamic Mechanical Analysis was performed on the pristine acrylic foam and on the composite foam showed a stiffening effect associated with the presence of cork granules, and a thermal transition centered at around −10 ◦C, associated with the acrylic binder’s glass transition. The surface has hardness slightly lower than cork, depending on the amount of particles incorporated. Pull-off testing consistently resulted in substrate failure, indicating that the coating’s cohesion and adhesion are excellent. The developed coating showed to have the intended functionality while being easily applicable on flat panel surfaces. The fact that a foam is used as a binder system allows for a smooth and soft surface, having excellent opacity with minimal usage of cork.
- Liquefied wood as a partial substitute of melamine-urea-formaldehyde and urea-formaldehyde resinsPublication . Esteves, Bruno; Martins, João; Martins, Jorge; Cruz-Lopes, Luísa; Vicente, José; Domingos, IdalinaMaritime pine (Pinus pinaster) sawdust was used to produce liquefied wood by the polyhydric method with acid catalysis. The process was optimized to produce the highest amount of liquefied wood. Wood liquefied at 160ºC for 90 min was used in the adhesion tests. The bond strength of veneer glued with urea-formaldehyde and melamine-urea-formaldehyde resins and several mixtures of liquefied wood with urea- formaldehyde and melamine-urea-formaldehyde wasevaluated by automated bonding evaluation system. With the increase in liquefied wood content the bond strength decreased. Nevertheless for 20% liquefied wood the reduction of internal bond strength is relatively small and still within the minimum standards required. When 70% of liquefied wood is employed there is a significant decrease in bond strength. In conclusion it is possible to use a small amount of maritime pine sawdust liquefied wood as a partial substitute of urea-formaldehyde and melamine-urea-formaldehyde resins in the particleboard production, thus decreasing the formaldehyde content.